MAVERICK X3 64" HIGH CLEARANCE WORX SERIES BILLET RADIUS ROD KIT by CT Raceworx
CT-X3-2210-0Free shipping with in the lower 48 states.
SKU: CT-X3-2210
Discover the pinnacle of performance with our high-clearance lower radius rods, engineered to elevate your off-road experience. Crafted from top-grade 7075-T6 aircraft aluminum, these rods offer over an inch of additional ground clearance, making them the strongest aluminum option in our sport. The FK 5/8" WSSX uniball joints, the same series used by trophy trucks, are housed at both ends, leaving no room for upgrades. What truly sets us apart in the industry is the exceptional quality of our joints. Our JMX series FK joints feature a fabric-based PTFE liner and a compressed inner joint housing, ensuring a preload on the ball that maintains tightness approximately three times longer than standard injected Teflon rod ends.
For extended joint life, we offer boots at an additional cost of $10 per joint, guarding against debris while allowing for added lubrication. Don't fall for cheap imitations with inferior materials and joints, as initial savings can lead to more significant time and money investments when those subpar joints wear out. Our 303 stainless steel spacers guarantee strength and corrosion resistance.
Once installed, this kit enables full adjustability of camber and toe at ride height. We take pride in using American products and materials exclusively, avoiding cheaper overseas alternatives. Notably, our lower radius rods made from 7075 aluminum offer remarkable strength compared to 6061, ensuring they won't elongate, stretch, bend, dent, or scratch. Plus, we back our aluminum parts with a lifetime warranty, providing you with peace of mind and unbeatable performance. Upgrade to the best; choose Ct for uncompromising quality and durability.
6061 Properties
Tensile Strength – 45,000 psi
Yield Point – 40,000 psi
Brinell Hardness – 95
Elongation at Break – 12%
Shear Strength – 31,000 psi
Strength to Weight Ratio: 115 kN-m/kg
7075 Properties
Tensile Strength – 83,000 psi
Yield Point – 74,000 psi
Brinell Hardness – 150
Elongation at Break – 10%
Shear Strength – 48,000 psi
Strength to Weight Ratio: 196 kN-m/kg
CB 5/22/25